NANOSCALE LUMINESCENT MATERIALS 2
卷 45, 期 5, 页码 43-48出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/1.3700408
关键词
-
资金
- Centre for Photonics, a division of Ontario Centres of Excellence Inc.
- Canadian Institute for Photonics Innovations (CIPI)
- Natural Sciences and Engineering Research Council of Canada (NSERC)
The luminescent and structural properties of cerium and terbium co-doped silicon oxide thin films were investigated through transmission electron microscopy, photoluminescence spectroscopy, and synchrotron-based X-ray absorption spectroscopy. While combined blue and green luminescence characteristic of Ce3+ and Tb3+ ions, respectively, was observed from different compositions of films, the emission intensity from samples in which Ce2Si2O7 nanocrystallites were formed after high temperature annealing was much stronger than in films where the Ce and Tb co-dopants were incorporated in an amorphous SiO2 host matrix. Films containing the cerium silicate phase also exhibited a very strong enhancement of Tb emission. X-ray absorption near edge structure and X-ray excited optical luminescence analysis at the Si L-3,L-2-, Si K-, O K-, Ce N-4-, and Ce M-5,M-4-edges indicated this enhancement was likely the result of a direct energy transfer process between the cerium silicate and Tb levels.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据