Introduction of pinning centers into Sm1+xBa2 Cu3+YO7-d coated conductor by reactive co-evaporation method

Sm1+xBa2Cu3+yO7-d (SmBCO)-coated conductors containing pinning centers were prepared by a reactive co-evaporation method using the EDDC (Evaporation using Drum in Dual Chamber) deposition system. Superconducting materials based on Sm, Ba, and Cu were evaporated in the evaporation chamber and deposited onto the drum-mounted substrate, while the deposited element reacted with oxygen and resulting in the SmBCO superconducting phase inside the reaction chamber. Tape-type samples (length= 30 cm, width = 4 mm, thickness = 0.1 mm) with the structure of Ag/SmBCO/LMO/MgO/Y2O3/Al2O3/Hastelloy were prepared, where the SmBCO film was spread along the tape length. The critical current was measured using the non-contact Hall-probe method, and the field dependences of the critical current under a high magnetic field were measured. The superconducting properties of the samples under a magnetic field were highly influenced by the composition of the SmBCO film. Furthermore, elemental mapping of the high-Jc SmBCO-coated conductor was measured by transmission electron microscopy coupled with energy-dispersive X-ray spectroscopy (TEM-EDX). Finally, we confirmed the Sm-related secondary phases take the role of pinning centers. (C) 2017 Elsevier B.V. All rights reserved.