期刊
PARTICULATE SCIENCE AND TECHNOLOGY
卷 36, 期 3, 页码 378-385出版社
TAYLOR & FRANCIS INC
DOI: 10.1080/02726351.2016.1262484
关键词
Aging; dental composite resin; microhardness; pH media; wear behavior
资金
- National Natural Science Foundation of China [81400483]
- Provincial Key Technology Research and Development Program of the Ministry of Science and Technology of Sichuan Province [2014SZ0037]
This study evaluated the microhardness and wear behavior alterations of dental resins exposed to strong acid and alkaline degradation regimens. Fifty specimens of AP-X, Z350, P60, VITA ZETA and VITA LC resins were distributed into 10 groups. The control group was not subjected to aging treatment, while the other nine groups were assigned to the following pH solutions: 1, 7 or 13 for 1, 13 or 20 d, respectively. Vickers microhardness and wear behavior of materials without aging served as the reference. Repeated measurements were conducted for other specimens. Scanning electron microscopy was used to observe the morphology. Data were analyzed by repeated-measures one-way ANOVA, followed by the least significant difference (LSD) t-test (P0.05) for multiple comparisons. The aging process was aggravated over time. Alkaline medium significantly decreased the microhardness and wear resistance of resins, and led to serious surface damage. AP-X, P60 and Z350 immersed in different media showed a lower degradation than the nanoresin. The mechanical degradation of resin composites was aggravated with increased aging time. Strong alkaline media induced the largest reduction in mechanical and tribological properties. Hybrid resin composites with high filler loading exhibited better mechanical performance than nanoresins with low filler loading under different pH conditions.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据