期刊
OPTICAL MATERIALS
卷 75, 期 -, 页码 770-780出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.optmat.2017.10.036
关键词
Photoluminescence; Double molybdate; Temperatures sensing; Thermal effect; Photothermal conversion efficiency
资金
- IIT(ISM) Dhanbad
- Council of Scientific & Industrial Research, New Delhi [03(1303)/13/EMR-II]
The photoluminescence properties of Yb3+ sensitized Er3+ doped BaLa2(MoO4)(4), SrLa2(MoO4)(4) and CaLa2(MoO4)(4) phosphors synthesized via hydrothermal method are investigated upon 980 nm and 380 nm light excitations. The phase, purity, and morphology of the samples are characterized by X-ray diffraction, Fourier transform infrared spectroscopy and Field emission scanning electron microscope. Among these three phosphors, the strongest emission intensity is seen in BaLa2(MoO4)(4): Er3+/Yb3+ through both the 980 nm and 380 nm light excitations and is explained by the lifetime measurement of S-4(3/2) level of Er3+ ion. Temperature sensing measurements were performed by using the fluorescence intensity ratio (FIR) of green emission bands originated from the two thermally coupled H-2(11/2) -> I-4(15/2) and S-4(3//2) -> I-4(15/2) transitions of Er3+ and maximum temperature sensitivity of 1.05% K-1 at 305 K is found for BLa2(MoO4)(4): Er3+/Yb3+ sample. Moreover, the laser induced heating is measured in the samples and the maximum temperature of the sample particles is calculated as 422 K at 76 W/cm(2) in BaLa2(MoO4)(4): Er3+/Yb3+, pointing out large amount of heat generation in such phosphors. The BaLa2(MoO4)(4): Er3+/Yb3+ also exhibits higher photothermal conversion efficiency of 46.7%. (C) 2017 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据