Nanoporous carbonaceous materials with high surface area were prepared by the pyrolysis of polymethyl(phenyl) siloxane resin (SR249) under vacuum at a controlled temperature (1 250-1 350 degrees C) followed by leaching in hydrofluoric acid (HF). Their compositions and structures at different pyrolysis temperatures were investigated by X-ray diffraction, Raman spectroscopy, elemental analysis, transmission electron microscopy and N-2 adsorption. The SiO2 phase in the pyrolysis products was regarded as a natural template and could be leached away by HF. The pyrolysis temperature and leaching had important effects on the compositions and structures of the carbonaceous materials. Their specific surface areas were very low (<55 m(2)/g) before leaching, but the specific surface area and total pore volume increased significantly after leaching, and could be as high as 1148m(2)/g and 0.608 cm(3)/g, respectively when pyrolysis was carried out at 1300 degrees C. The pore size of all the samples after leaching was in the narrow range of 1-4 nm. TEM showed that the free carbon phase, SiC nanocrystallines and silicon oxycarbide ceramics wrapped each other.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据