期刊
JOURNAL OF SEMICONDUCTORS
卷 34, 期 10, 页码 -出版社
IOP PUBLISHING LTD
DOI: 10.1088/1674-4926/34/10/103001
关键词
vanadium oxide; thin films; optical properties; cycle voltammogram
Vanadium oxide thin films were prepared on glass substrates by using the spray pyrolysis technique. The effect of solution concentration (0.1 M, 0.2 M and 0.3 M) on the nanostructural, electrical, optical, and electrochromic properties of deposited films were investigated using X-ray diffraction, scanning electron microscopy, UV-vis spectroscopy, and cyclic volta-metrics. The X-ray diffraction shows that only the sample at 0.1 M has a single beta-V2O5 phase and the others have mixed phases of vanadium oxide. The lowest sheet resistance was obtained for the samples prepared at 0.3 M solution. It was also found that the optical transparency of the samples changes from 70% to 35% and the optical band gap of the samples was in the range of 2.20 to 2.41 eV, depending on the morality of solution. The cycle voltammogram shows that the sample prepared at 0.3 M has one-step electerochoromic but the other samples have two-step electerochoromic. The results show a correlation between the cycle voltammogram and the physical properties of the films.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据