Ordered mesoporous carbon; Graphene oxide; Gas adsorption; Benzene vapor; Hydrogen; Carbon dioxide; Methane
类别
资金
- National Science Centre (Poland) [UMO-2016/23/B/ST5/00532]
Graphene oxide/ordered mesoporous carbon (GO/OMC) nanostructures with narrow mesopore size distribution were obtained via soft-templating synthesis followed by KOH activation. Microporosity and mesoporosity of. these composite nanostructures were additionally controlled by adjusting the amount of added GO and by post-synthesis KOH activation, Incorporation of GO into OMC structure resulted in improving absorption uptakes of benzene and hydrogen, which reached 9.6 mmol/g (at 20 degrees C and pressure close to the saturation vapor pressure) and 11.7 mmol/g (2.3 wt% H-2 at -196 degrees C and 760 mm Hg), respectively. At the same conditions bare activated OMC adsorbed 8.1 mmol/g and 10.8 mmol/g of benzene and hydrogen, respectively. Also, these adsorbents showed high uptakes of CH4 (2.1 mmol/g at 20 degrees C and 760 mm Hg) and CO2 (6.0 mmol/g at 0 degrees C and 760 mm Hg). The GO/OMC composite nanostructures, were characterized by nitrogen adsorption, scanning electron microscopy, Raman spectroscopy and thermogravimetry. To the best of our knowledge, this work represents the, first comparative study of adsorption properties of the GO/OMC composite nanostructures toward various gases.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据