ADVANCES IN NATURAL SCIENCES-NANOSCIENCE AND NANOTECHNOLOGY
卷 4, 期 4, 页码 -出版社
IOP PUBLISHING LTD
DOI: 10.1088/2043-6262/4/4/045011
关键词
pulsed laser ablation; gold; silver; nanoparticles; supercritical CO2
资金
- Grants-in-Aid for Scientific Research [21246119, 21110004, 21110009] Funding Source: KAKEN
Pulsed laser ablation (PLA) has become a promising method for the synthesis of nanoclusters for photonics, electronics and medicine. In this work PLA in pressurized CO2 has been applied for fabrication of gold and silver nanoparticles. Laser ablation was performed with an excitation wavelength of 532 nm under various pressures (0.1-20MPa), temperatures (40-80 degrees C) of CO2 medium and ablation times (1500-9000 s). On the basis of the experimental result, it follows that structures of gold (Au) and silver (Ag) nanoparticles were significantly affected by the changes in CO2 density. The structures of gold and silver nanoparticles also changed with an increase of ablation time. From a field-emission scanning electron microscopy (FE-SEM) image of the fabricated gold nano-structured particles on silicon wafer, it was seen that a network structure of smaller gold particles was fabricated. A similar morphology of particles fabricated from silver plate was observed. Silver particles contain nanoparticles with large-varied diameter ranging from 5 nm to 1.2 mu m. The mechanism of nanoparticles fabrication could be observed as follows. Bigger gold/silver particles melted during the ablation process and then ejected smaller spherical nanoparticles, which formed nanoclusters attached on the molten particles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据