MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING
卷 80, 期 -, 页码 111-117出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.mssp.2018.02.026
关键词
ZnO; Ion implantation; Raman spectroscopy; Photoluminescence; Acceptors
类别
资金
- University Grant Commission (UGC), Government of India [520642]
Doping lithium (Li) and/or nitrogen (N) in ZnO and activation of shallow acceptors thereby have drawn specific scientific interest for the last few years. A comprehensive study employing Raman spectroscopy is being reported here on N and Li implantation effects in ZnO. Strong presence of 275 cm(-1) Raman mode after N and (Li, N) implantation confirms its relation with doped nitrogen in ZnO. Weak presence of 510 cm(-1) mode in the high fluence implanted ZnO indicates its origin with interstitial defects. No extra Raman mode has been identified in Li implanted samples. Raman mode with anomalously large intensity is found at 1562 cm(-1) after (Li, N) co-implantation (highest fluence). Implantation causes huge increase of Raman modes similar to 540, 555 and 579 cm(-1), with the last two bearing clear co-relations with interstitial Zn and O vacancy, respectively. To identify shallow acceptors due to dopant-defect complex, low temperature photoluminescence (PL) has been monitored but only donor related excitonic features are visible in the near band edge (NBE) emission. However, indications in favour of deep acceptors states are noted, particularly when Li is present in the sample. The deep acceptor level may be at similar to 300 meV above the valence band consistent with previous results.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据