DOI: 10.1016/j.msea.2017.11.063
关键词
Selective laser melting; Al-Cu-Mg-Si alloy; Heat treatment; Microstructure; Mechanical properties
类别
资金
- Chinese Scholarship Council (CSC)
- European Research Council under the ERC Advanced Grant INTELHYB [ERC-2013-ADG-340025]
A heat-treatable Al-3.5Cu-1.5Mg-1Si alloy is successfully fabricated by selective laser melting and is investigated concerning microstructures and mechanical properties. The as-prepared samples show a fine-granular microstructure in the individual melt pool of the tracks and a coarse-granular microstructure in the areas between the tracks. After T6 heat treatment, the grain size of the specimens increases slightly and the Q phase formed in the as-prepared specimens transforms to Al2Cu(Mg), Mg2Si, and AlxMny. All Al-Cu-Mg-Si specimens before and after heat treatment fracture around the defects that were generated during processing and show intergranular fracture along columnar grains upon tensile quasi-static loading. The as-fabricated samples exhibit a yield strength (YS) of 223 +/- 4 MPa and an ultimate tensile strength (UTS) of 366 +/- 7 MPa with an elongation of 5.3 +/- 0.3%. After T6 heat treatment, the YS and UTS increase dramatically to 368 +/- 6 MPa and 455 +/- 10 MPa due to the formation of nano-sized Al2Cu(Mg) precipitates, while the ductility remains fairly similar.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据