Nb micro-alloying; TWIP steel; Mechanical properties; Recovery annealing
类别
资金
- CBMM
- POSCO Technical Research Laboratories
We investigated the effect of Nb micro-alloying in the range of 0.01 to 0.1 wt% on the microstructures and mechanical properties of Fe17Mn0.6Cl.5Al (wt%) TWIP steel. EBSD analysis shows that the Nb addition retards recrystallization in both the hot-rolled steels and cold-rolled and annealed steels. The Nb addition in the cold rolled and annealed TWIP steel leads to an increase in yield strength. This phenomenon is due to a combined effect of precipitation hardening and a low degree of recrystallization. Recovery annealing of the cold-rolled TWIP steels at 650 degrees C results in a good combination of yield strength and ductility. The steels containing 0.01 wt % and 0.025 wt% of Nb show a superior combination of UTS x TE exceeding 40,000 MPa.% and yield strength higher than 800 MPa. The design of TWIP steels utilizing both precipitation hardening and partial re crystallization opens a way to develop steels with a superior combination of yield strength and ductility.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据