DOI: 10.1016/j.msea.2018.01.057
关键词
Nickel aluminide, spherical powder; High-resolution electron microscopy; Guinier-Preston zones; Creep
类别
资金
- Ministry of Education and Science of the Russian Federation [14.578.21.0260, RFMEFI5817X0260]
- Federal Target Program Research and Development in the Priority Development Areas of the Russian Science and Technology Sector
The microstructure of Ni alloy produced by hot isostatic pressing (HIP) and selective laser melting (SLM) using pre-alloyed Ni41Al41Cr12Co6 spherical powders was studied by scanning electron microscopy (SEM) and high resolution electron microscopy (HRTEM). In-situ studies of the evolution of the fine structure of Ni41Al41Cr12Co6 alloy during the heating at 20,350... 850 degrees C has been performed. Homogeneous precipitation and growth of the spherical Guinier-Preston zones rich in Cr (size < 5 nm) on concentration fluctuations of dopants in the beta-NiAl matrix by spinodal decomposition was detected in the range of 20-450 degrees C. In addition, the precipitation of the Guinier-Preston zones by heterogeneous nucleation on the crystalline defects of beta-NiAl matrix has been revealed. Prismatic dislocation loops 10-25 nm in size with a stacking fault are formed from a vacancy cluster in the beta-NiAl grain at 750 degrees C. In the 750-850 degrees C interval, heterogeneous nucleation and growth of alpha-Cr nanocrystallites having a prismatic shape and longitudinal size of 20-50 nm was observed on the prismatic dislocation loops. Also, high-temperature strength characteristics of the alloy produced by HIP in the temperature range of 600-1100 degrees C on a Gleeble System 3800 testing system was studied. The high-temperature strength of the HIP samples produced using pre-alloyed spherical powders is higher by 80-100 MPa compared to that of the as-cast alloy.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据