Explosive welding; Mg/Al composite plates; Multi-pass rolling; Annealing; Mechanical properties
类别
资金
- Natural Science Foundation Project of China [51375328]
- Shanxi Scholarship Council of China [2015036]
In this study we investigated the effect of multi-pass rolling and post-rolling heat treatment upon the microstructure at interface and mechanical properties of the explosive welding Mg/Al composite plates. The thin explosive welding Mg/A1 composite plates with 2.14 mm in thickness and good surface quality were obtained by 5 passes hot rolling (30% reduction, 400 degrees C). To meet the requirement of subsequent forming, annealing process was performed. The results indicate that the thickness of interfacial diffusion layer increases with the increase of annealing temperature and holding time. The mechanical properties of composite plates increase first and then decrease with the increase of annealing temperature and holding time. The tensile strength and elongation of the composite plates under 200 degrees C/2 h annealing condition reach the maximum, which are 285 MPa and 24.5% respectively. Fracture surface morphology indicates that the post-rolling or annealed composite plates all exhibit mixed-mode of ductile and brittle fractures.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据