Crystallographic characterization of laser-generated, polymer-stabilized 4 nm silver-gold alloyed nanoparticles

Monometallic silver and gold nanoparticles and bimetallic silver-gold (AgAu) nanoparticles were prepared by laser ablation in liquids in the atomic composition range of Ag:Au from 0:100 to 100:0 with steps of 10 at% and colloidally stabilized with poly(N-vinylpyrrolidone) (PVP). As metallic bulk targets for laser ablation, pure silver, pure gold, and alloyed AgAu foils with the desired composition were used. Size separation by centrifugation and freeze-drying gave monodisperse spherical nanoparticles with a diameter of 4 nm as determined by differential centrifugal sedimentation (DCS) and transmission electron microscopy (TEM). A crystallographic characterization of the nanoparticles was carried out by X-ray powder diffraction (XRD) and Rietveld refinement, leading to highly precise cubic lattice parameters (fcc crystal system) and crystallite sizes. For comparison, the same analysis including the determination of the microstrain was carried out for the bulk target materials (AgAu alloys in the full concentration range). Both nanoparticles and bulk target materials obeyed Vegard's rule, with only slight deviations. The fact that the crystallite size as determined by XRD was identical to the hydrodynamic diameter by DCS and the Feret diameter by TEM indicates that the particles consist of only one domain, i.e. they are single crystals. The combination of UV-vis spectroscopy with energy-dispersive X-ray spectroscopy (EDX) as line scan along the nanoparticle showed a homogenous distribution of the gold and silver inside the nanoparticles, indicating solid solution alloys, in contrast to what was observed earlier for chemically prepared AgAu nanoparticles by reduction of metal ions in water. (C) 2018 Elsevier B.V. All rights reserved.