This paper reports the synthesis of hierarchical meso/macroporous TiO2 scaffolds by mimicking bone structure. Evaporation-induced self-assembly (EISA) method along with foamy method was utilized to produce TiO2 scaffolds in situ. Simultaneous thermal analysis (STA), small angle X-ray diffraction (SAXD), wide-angle X-ray diffraction (WAXD), nitrogen adsorption-desorption isotherm analysis, scanning electron microscopy (SEM) and transmission electron microscopy(TEM) techniques were applied to characterize the scaffolds. The results showed that TiO2 scaffolds can be produced after sintering the specimens at 550 degrees C for 2 h. The obtained scaffolds had a pore size in the range of 150-300 pm and meso pores in the range of 6-12 nm. The specific surface area was obtained from the Brunauer-Emmett-Teller theory, the total volume and mean diameter of pores were 67.89 m(3) g(-1), 0.1245 cm(3) g(-1) and 7.3 nm, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据