MATERIALS CHARACTERIZATION
卷 136, 期 -, 页码 388-397出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.matchar.2018.01.008
关键词
ASTM Grade P92 steel; Isothermal ageing; Mechanical properties; Creep testing; Microstructure evolution; Creep life
类别
资金
- Czech Science Foundation [16-09518S]
- Ministry of Education, Youth and Sports of the Czech Republic [LM2015069]
We have investigated the effect of prior short-term ageing on the mechanical and creep properties of tungsten and boron modified 9%Cr ferritic steel (ASTM Grade P92 steel), to provide material data base for the estimation of material degradation due to occurrence of accidental overheating in the early stage of service loading. The steel was aged at 650 degrees C for up to 100, 200, 500, 1000, 2000 and 5000 h prior to mechanical and creep testing. Changes in the microstructure during ageing had a slight effect on the reduction of room temperature tensile properties. A sudden decrease on impact properties occurred after ageing for 2000 h, but the occurred impact energy of about 70 J is in accordance with the specified minimum value of 68 J at room temperature for the virgin condition. The creep behaviour of P92 steel in the as-received condition and after different isothermal ageing exposures prior to creep was investigated at 600 and 650 degrees C in the power-law creep regime. The initial applied tensile stress ranged from 90 to 200 MPa. The results clearly show a detrimental influence of isothermal ageing on creep properties even after a few hundred hours. Based on microstructure analysis, which was done mostly in a qualitative way, a significant decrease in the creep life after ageing resulted from changes of the dislocation substructure and instability of Laves phase and M23C6 particles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据