JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS
卷 32, 期 6, 页码 831-847出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0892705718780964
关键词
M-aramid; ionomers; composites; thermal properties; mechanical properties
资金
- Technology Innovation Program - Ministry of Trade, Industry & Energy (MOTIE Korea) [10076409]
- Yeungnam University
- Korea Evaluation Institute of Industrial Technology (KEIT) [10076409] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
Novel hybrid blend with the composition of m-aramid and sodium ionomers with different weight ratio percentage were prepared by the solution blending technique. The prepared composite films were characterized by the Fourier-transform infrared (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry, thermogravimetric analysis (TGA), and dynamic mechanical analysis (DMA). The phase structure, compatibility, and morphologies of the composite film were investigated with SEM, DMA, XRD, and transmission electron microscopy (TEM) analysis. The TGA of the composite films shows improvement in the thermal stability. The temperature corresponding to 5% (T (5%)) weight losses is in the range of 101-414 degrees C. The storage modulus (in the range of 01.55-3.0 GPa) and glass transition temperature (in the range of 244-276 degrees C) decreased with an increase in the content of sodium ionomers. The tensile strength of the composite films is in the range of 160-185 MPa. This effective approach shows a potential application in the field of m-aramid-based composites.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据