Polyetheramine; Composite hollow fiber membrane; CO2 removal; Interfacial polymerization
PEAm-TMC/PDMS/PVC composite hollow fiber membrane for CO2 separation was developed through interfacial polymerization (IP) on the PDMS pre-coated inner surface of PVC hollow fiber. Polyetheramine (PEAm) and Trimesoyl chloride (TMC) were selected as aqueous monomer and organic monomer, respectively. SEM observation result shows that the thickness of PEAm-TMC IP layer is about 215 nm. The effects of monomer concentrations and acid acceptor concentration on the membrane performance were investigated. The results shows that the CO2 permeance decareses and CO2/N-2 selectivity increases with the increasing concentrations of PEAm, TMC and Na2CO3. At 0.12 MPa, the composite hollow fiber membrane possesses a very high CO2 permeance of 964 GPU and CO2/N-2 selectivity of 40.6.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据