期刊
FATIGUE DESIGN 2013, INTERNATIONAL CONFERENCE PROCEEDINGS
卷 66, 期 -, 页码 226-232出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.proeng.2013.12.077
关键词
Fatigue crack growth; temperature; thermal ageing
资金
- French National Research Agency (ANR)
The high-temperature Fatigue Crack Growth (FCG) behaviour of a 15-5 PH (precipitation-hardened) martensitic stainless steel was investigated in three different metallurgical conditions, i.e., as-received, aged at 300 degrees C for 1000h and 5000h. FCG tests were conducted at room temperature and 300 degrees C under constant amplitude loading with two load ratios (R = 0.1 and 0.7) and under variable amplitude loading. The results indicate that the fatigue crack growth rates (FCGRs) increase with R-ratio at the lower Delta K regime and merge together in the high Delta K regime, regardless of ageing conditions and temperature. At 300 degrees C, the FCGRs are higher than at room temperature for all ageing conditions. Under variable amplitude loading, the same retardation effect was observed for all the given ageing conditions at room temperature (C) 2013 The Authors. Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据