JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 38, 期 14, 页码 4707-4718出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2018.06.014
关键词
Lithium garnet; Air exposure; Phase (in)stability; Structural (in)stability; Mechanical (in)stability
资金
- IRCC (IIT Bombay, India) [RI/0215-10001195-001]
Among the Li-ion conducting inorganic materials, lithium lanthanum zirconate (LLZO) is believed to possess good chemical stability against Li metal and hence considered to be a promising solid electrolyte for Li-ion batteries. However, systematic sets of studies conducted here at regular intervals during storage of Al-doped LLZO (cubic garnet) sintered pellets in ambient atmosphere have raised serious concerns over their structural/ mechanical stability/integrity upon exposure to air. Spontaneous cracking/disintegration/pulverization of LLZO pellets takes place after about three weeks of exposure, primarily due to formation of La2Zr2O2 in the LLZO bulk; as found to be thermodynamically feasible at room temperature upon reaction with CO2/moisture. Steep increase in ZrLa2Zr2O2 content coincides with the spontaneous cracking/disintegration. Estimation suggests that internal stresses associated with the formation of La2Zr2O2 from LLZO can be high enough to cause spontaneous fracture. This mandates the development/fabrication/usage of solid-state cells using LLZO under stringent controls against exposure to atmospheric species.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据