JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 38, 期 9, 页码 3089-3095出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2018.02.041
关键词
High-energy milling; Hardness; Strength; Solid solution; Armour materials
B4C-TiB2 composites were contaminated with WC to study the effect on densification, microstructure and properties. WC was introduced through a mild or a high energy milling with WC-6 wt%Co spheres or directly as sintering aid to 50 vol% B4C / 50 vol%TiB2 mixtures. High energy milling was very effective in improving the densification thanks to the synergistic action of WC impurities, acting as sintering aid, and size reduction of the starting TiB2-B4C powders. As a result, the sintering temperature necessary for full densification decreased to 1860 degrees C and both strength and hardness benefited from the microstructure refinement, 860 +/- 40 MPa and 28.5 +/- 1.4 GPa respectively. High energy milling was then adopted for producing 75 vol% B4C/25 vol% TiB2 and 25 vol% B4C/ 75vol%TiB2 mixtures. The B4C-rich composition showed the highest hardness, 32.2 +/- 1.8 GPa, whilst the TiB2-rich composition showed the highest value of toughness, 5.1 +/- 0.1 MPa ma(0.5).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据