期刊
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 38, 期 10, 页码 3417-3423出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2018.03.009
关键词
Ti3AlC2; Texture microstructure; Oxidation behavior; Oxidation mechanisms
资金
- Chu-Ying program of Southwest Jiaotong University
- Thousand Talents Programs of China and Sichuan Province
- Fundamental Research Funds for the Central Universities [2682016CX071]
- Natural Sciences Foundation of China [51741208]
- Japan Society for the Promotion Science [23350104]
- Korean Institute of Materials Science (KIMS)
Oxidation resistance of textured Ti3AlC2 ceramics was measured in the temperature range 1273-1573 K It was found that the oxidation was markedly anisotropic and the samples exhibited a better oxidation resistance when tested along a direction transverse to the c-axis. This behavior was attributed to the rapid diffusion of A1 within its basal planes to form a passivating Al2O3 scale and it respected Ellingham diagrams. The scales formed had different compositions depending on the testing direction, this response was clearly resulting from the crystal lographic orientation. Even at 1473 K after 20 h exposure, the samples tested in a direction transverse to the c-axis showed a reduced weight gain which was 45 times lower than one seen on a basal plane.