JOURNAL OF PHYSICAL CHEMISTRY C
卷 122, 期 11, 页码 5935-5939出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.jpcc.8b00341
关键词
-
资金
- DFG [GRK 1896]
Hybrid organic-inorganic perovskites have emerged as cost-effective and high-performance semiconductors for optoelectronic applications. Precise knowledge of charge carrier mobility and especially the temperature dependence of mobility is therefore of utmost relevance for advancing high-performance materials. Here, the charge carrier mobility in methylammonium lead iodide single crystals is investigated with time of flight technique from 290 to 100 K. A nondispersive transport with an electron mobility of 135 (+/- 20) cm(2)/V s and a hole mobility of 90 (+/- 20) cm(2)/V s is obtained at room temperature. A power-law temperature dependence of mobility, mu alpha T-m, with an exponent m = -2.8 and -2.0, is measured for electrons and holes in the tetragonal phase. The highest electron and hole mobilities measured are 635 (+/- 70) and 415 (+/- 20) cm(2)/V s, respectively. Our results indicate that the scattering of charge carriers with phonons is the limiting factor for carrier mobilities at room temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据