JOURNAL OF NUCLEAR MATERIALS
卷 502, 期 -, 页码 282-288出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jnucmat.2018.02.017
关键词
-
资金
- Euratom research and training programme [633053]
The C, N, and W content in EUROFER97, a 9CrWVTa reduced-activation ferritic/martensitic (RAFM) steel, was varied to obtain an experimental assessment of the main effects of the compositional variation on the mechanical properties and microstructural characteristics of six different experimental grades. Light optical microscopy (LOM) and electron back-scattered diffraction (EBSD) revealed in almost all cases a fine tempered lath martensite structure. Analyses of transmission electron micrographs, together with inductively coupled plasma mass spectrometry (ICPMS) and energy-dispersive x-ray spectroscopy (EDS) data, shows the precipitation state and spatial distribution of MxCy (M = Cr, W and Fe) and MX (M = V and/or Ta, X = C or N) carbonitrides within the matrix. The mechanical characterization of the six different steel grades was carried out by means of A50 tensile testing and Charpy tests on standard specimens (55 x 10 x 10 mm(3)). Lowering the carbon content and keeping the nitrogen content higher than 0.02 wt%, leads to a reduction of the ductile-to-brittle-transition-temperature (DBTT) in comparison with EUROFER97-2. The addition of tungsten further reduces the DBTT to -94 degrees C, while maintaining good tensile strength and elongation. (c) 2018 University of Ghent (UGent). Published by Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据