NiFe2O4/SiO2 Nanocomposites; Solution Combustion and Calcination Process; Grain Size; Saturation Magnetization
A facile solution combustion and calcination process for the preparation of magnetic NiFe2O4/SiO2 nanocomposites was introduced, the as-prepared NiFe2O4/SiO2 nanocomposites were characterized by XRD, VSM, BET, FTIR, SEM, and TEM techniques. The results showed that the single ferrite phase of NiFe2O4 could be formed at 400 degrees C; the calcination temperature, the content of silica in nanocomposites, and the volume of absolute alcohol were three key factors to the properties of the magnetic NiFe2O4/SiO2 nanocomposites: with the volume of absolute alcohol increasing from 10 mL to 100 mL, the average grain size of NiFe2O4/SiO2 nanocomposites calcined at 400 degrees C for 2 h with the heating rate of 3 degrees C/min decreased from about 16.6 nm to 8.4 nm, while the saturation magnetization decreased from about 6.1 Am-2/kg to 1.5 Am-2/kg; with the calcination temperature increasing from 400 degrees C to 800 degrees C, the average grain size of NiFe2O4/SiO2 nanocomposites calcined for 2 h with the heating rate of 3 degrees C/min and absolute alcohol of 30 mL increased from about 11.0 nm to 14.1 nm, and the saturation magnetization increased from about 3.4 Am-2/kg to 24.0 Am-2/kg; at the same time, with the content of silica in nanocomposites increasing from 0 to 10 wt.%, the average grain size of NiFe2O4/SiO2 nanocomposites calcined at 400 degrees C for 2 h with the heating rate of 3 degrees C/min decreased from about 18.4 nm to 11.0 nm, while the saturation magnetization decreased from about 18.2 Am-2/kg to 3.4 Am-2/kg.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据