期刊
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
卷 255, 期 -, 页码 673-678出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jmatprotec.2018.01.022
关键词
Superalloy; Eutectic; Transient liquid phase; Joining
The amount of gamma/nickel boride/Ni-B-Si ternary eutectic in the athermally solidified zone of joints was increased with increased thickness of the filler metal. By increasing the temperature from 1130 degrees C to 1160 degrees C, isothermal solidification was completed and no harmful phase was found in the middle of the joints. At higher temperatures, the dissolution of substrate elements prevented the diffusion of melting point depressants and the eutectic phase reappeared. Solidification cracks were observed when transient liquid phase bonding was done in non-vacuum atmospheres. The peak hardness in diffusion affected zones remained even when isothermal solidification was completed. The maximum shear strength of 412 MPa was achieved for a specimen with complete isothermal solidification (50 mu m/1160 degrees C/45 min).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据