In this study, the effect of flexural loading on the chloride-induced corrosion behavior of steels in large-sized concrete was characterized using various electrochemical methods and X-ray computed tomography (X-CT). Electrochemical measurements revealed that steels embedded in loaded concrete exhibited higher corrosion rate than those in unloaded concrete after 15days of accelerated corrosion. However, after accelerated corrosion for 60days, similar corrosion behavior was identified for steels in both loaded concrete and unloaded concrete. It was found that the penetration and the distribution of corrosion products in concrete were significantly affected by the sustained flexural loading after the occurrence of load-induced transverse cracks. (c) 2018 American Society of Civil Engineers.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据