Cr3+ photoluminescence; Garnets; Near infrared emitting phosphors; Racah parameters; Thermal quenching; Phosphor converted LEDs; On-chip phosphor; 3d-3d emission
类别
资金
- Merz Pharmaceuticals GmbH
Broad band near-infrared (NIR) light sources have great potential, e.g., in optical communication and non-invasive medical imaging. Here we report the optical properties of X3Sc2Ga3O12 (X= Lu, Y, Gd, La) garnets doped with Cr3+ showing efficient T-4(2) -> (4)A(2) broad band NIR emission between 600 and 1000 nm. The chromium-doped garnets were investigated in view of their capability for blue to NIR conversion in high power phosphor converted LEDs (pcLEDs). Typical high power (In, Ga) N LEDs reach junction temperatures up to 450 K. Hence, the photoluminescence (PL) quenching temperature is a crucial parameter for on-chip phosphors. The Cr3+-doped garnets reveal very high quenching temperatures for the broad band NIR emission, similar to 700 K for Lu3Sc2Ga3O12, Y3Sc2Ga3O12, Gd3Sc2Ga3O12, and 450 K for La3Sc2Ga3O12. The high quenching temperatures are in line with a small Stokes shift (similar to 2400 cm(-1)) and weak electron-phonon coupling. To gain further insight in the luminescence properties, low temperature photoluminescence measurements were done. The optical properties of Cr3+ ions in garnets were analyzed in terms of the crystal field strength, Racah parameters, and phonon coupling parameters. The suitability for application in pcLEDs for high power broad band NIR sources was confirmed by emission measurements of ceramic pellets upon blue LED excitation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据