期刊
JOURNAL OF CHEMICAL SCIENCES
卷 126, 期 4, 页码 1013-1020出版社
INDIAN ACAD SCIENCES
DOI: 10.1007/s12039-014-0659-z
关键词
Ethanol; ethyl acetate; copper phyllosilicate; lewis acid sites
资金
- Natural Science Foundation of Science and Technology Department of Jilin Province [20130101015JC]
- State Key Laboratory of Inorganic Synthesis and Preparative Chemistry of Jilin University
- Innovation Project for the Frontiers of Science
- Jilin University
Cu/SiO2 catalysts that contain copper phyllosilicate, were successfully prepared using the ammonia-evaporation method. The catalysts were characterized via XRD, ICP, BET, FTIR, TPR, XPS, NH3-TPD and FTIR of Pyridine Adsorption techniques. The results demonstrated that the formation of the copper phyllosilicate species significantly affected the structural properties and caused the CuO nanoparticles to become highly dispersed, and the copper phyllosilicate would provide access to the Lewis acidic Cu+ species. It was found that the catalyst with a 23.7 wt% copper loading exhibited the best ethanol conversion and ethyl acetate selectivity. When compared to a catalyst with the same copper loading which was prepared with the impregnation method, the higher activity and selectivity of catalysts might be ascribed to the homogenous distribution of copper nanoparticles, which was the active site for the dehydrogenation, and the amount of Lewis acidic Cu+ sites active for esterification. The synergetic effect between the Cu-0 and Lewis acidic sites was the key factor to achieve direct transformation of ethanol to ethyl acetate.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据