JOURNAL OF AEROSPACE TECHNOLOGY AND MANAGEMENT
卷 6, 期 4, 页码 389-394出版社
INST AERONAUTICA & ESPACO-IAE
DOI: 10.5028/jatm.v6i4.400
关键词
Maraging steel; Cold rolling; Hardness test; Aging
Maraging steels have low carbon content and are highly alloyed, having as main feature the ability to increase the mechanical strength after thermal aging. Therefore, the objective of this work is to analyze the effect of aging in a Cofree maraging steel, Fe - 0.014% C - 0.3% Mn - 3.9% Mo 2.1% Cu - 0.19% Si - 11.8% Cr - 9.1% Ni - 1.0% Ti (wt), at different heat treatment times 10 min - 960 min) at constant temperature 550 degrees C), after cold rolling up to 66% and 77% area reduction. Microstructures were analyzed by scanning electron microscopy SEM - EDS) and mechanical properties by Vickers hardness measurements. The results showed a significant increase in the hardness of the material after aging heat treatment on the solution treated and deformed samples. The aging heat treatment which was harder about 650 HV was 550 degrees C/60 min.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据