期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 766, 期 -, 页码 1080-1085出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2018.07.048
关键词
High entropy alloy; Combinatorial thin film deposition; Oxidation; Diffusion; Atom probe tomography; Transmission electron microscopy
资金
- AHEAD project (DFG/ANR) [LU 1175/22-1]
Atom probe tomography was combined with transmission electron microscopy to characterize in atomic detail the structure of nanocrystalline high entropy alloy CrMnFeCoNi thin films before and after exposure to air at 500 degrees C for 5 min. Mn and Cr oxide scales were observed on the surface of the sample. These results on the nanoscale for short experimental time agree with literature reports on bulk counterparts after oxidation at 900 degrees C for 100 h, which means that the oxidation performance of complex materials can be tested in an accelerated way. Moreover, oxidation-related sub-surface depletion of Mn and Cr together with partial decomposition of the initial Cantor phase yield a FeCo-B2 sub-surface phase. In comparison to coarse-grained bulk material, the faster oxidation of the nanocrystalline material was attributed to an enhanced outwards diffusion of Cr and Mn along grain boundaries and within the newly formed B2 phase. (c) 2018 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据