JOURNAL OF ALLOYS AND COMPOUNDS
卷 741, 期 -, 页码 1112-1120出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2018.01.279
关键词
Ti2AlNb-based alloy; High energy ball-milling; Spark plasma sintering; Tensile property
资金
- Program for Changjiang Scholars and Innovative Research Team in University [IRT1229]
- National Natural Science Foundation of China [51275129]
A high strength and ductility Ti-22Al-25Nb alloy was fabricated from high energy ball-milled powder by spark plasma sintering. The pre-alloyed powder with a normal composition (at %) of 53 Ti, 22 Al and 25 Nb was firstly ball-milled for different milling times, and subsequently consolidated by spark plasma sintering. The effects of ball-milling time on the microstructure and mechanical properties of the ball-milled powder and sintered compact were investigated. The Ti-22Al-25Nb alloy sintered by SPS at 950 degrees C for 10 min under a pressure of 50 MPa from the ball-milled powder showed the microstructure with a large amount of ultrafine/nano O-phase. The best balance of tensile properties was exhibited in the Ti-22Al-25Nb alloy sintered from the ball-milled powder for 20 h; the yield strength, the tensile strength and the elongation to failure were 1092 MPa, 1105 MPa and 9.4% at room temperature respectively, exceeding other coarse grain Ti-22Al-25Nb alloys fabricated by other powder metallurgy methods in the comprehensive tensile property. The precipitation of secondary phase, the grain refinement and the change of residual dislocation density in the sintered alloy directly affected the tensile properties of the sintered alloy. (C) 2018 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据