期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 750, 期 -, 页码 857-862出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2018.04.009
关键词
C-f/SiC; ZrB2-SiC ceramics coating; Brushing process; Anti-ablation mechanism
资金
- National Science Foundation of China [51402357, 51602347]
In order to improve the oxidation behavior of C-f/SiC composites in oxygen atmosphere at high temperatures, ZrB2-SiC ceramics coatings were prepared on Cf/SiC composites by using a brushing process. The composition of the coating and the microstructure of the reaction products were investigated by XRD and SEM; the ratio of ZrB2: PCS was studied, and the anti-ablation test was used to analyze the stability of coating at higher temperature. The results showed that the coatings were homogenous by this method. The coatings could improve the stability effectively, when the ratio of ZrB2: PCS was 5:1, the coatings had the best interface combine intensity. Compare with the uncoated C-f/SiC samples, the coated C-f/SiC samples exhibited better anti-ablative property, the coating prevented the matrix from ablation efficiently. (C) 2018 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据