ISIJ INTERNATIONAL
卷 58, 期 3, 页码 488-495出版社
IRON STEEL INST JAPAN KEIDANREN KAIKAN
DOI: 10.2355/isijinternational.ISIJINT-2017-593
关键词
Mg dissolution; MgO-C refractory; spinel; inclusion
资金
- Iron and Steel Institute of Japan (ISIJ Research Promotion Grant)
- Technical Association of Refractories of Japan
MgO-C refractory is a widely employed refractory in steel refining and it is considered as a Mg source to form MgO center dot Al2O3 spinel inclusions in steel melt. In this study, MgO-C refractories with various carbon contents were immersed into Al-killed molten steel to investigate the dissolution behavior of Mg from MgO-C refractory. The result showed that Mg gradually dissolved into the steel melt from the refractory, and spinel inclusions were formed. Al in the steel melt reduced MgO in the refractory and consequently, Mg was dissolved into the steel melt. The dissolved Mg increased with the Al content in the steel melt. Moreover, C in the MgO-C refractory also reduced MgO in the refractory and supplied Mg to the steel melt. However, when the C concentration in the refractory was lower than 10 mass%, Mg was not supplied. The reduction in MgO by Al and C occurred independently, and the Mg content in the steel was the sum of the Mg supplied by these reactions. In some regions at the refractory steel melt interface, a spinel layer was observed; however, this layer was not formed uniformly.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据