JOURNAL OF MAGNESIUM AND ALLOYS
卷 2, 期 4, 页码 335-341出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jma.2014.11.004
关键词
Magnesium alloy; Stress corrosion cracking; Strain rate; Pitting corrosion
资金
- National Natural Science Foundation of China [51171192, 51271183, 51301172]
- National Basic Research Program of China (973 Program) [2013CB632205]
- Innovation Fund of Institute of Metal Research (IMR), Chinese Academy of Sciences (CAS)
Through performing the tensile tests with different strain rates in 3.5 wt.% NaCl solution, the stress corrosion cracking (SCC) behavior and the effect of strain rate on the SCC susceptibility of an extruded Mg-7% Gd-5% Y-1% Nd-0.5% Zr (EW75) alloy have been investigated. Results demonstrate that the alloy is susceptible to SCC when the strain rate is lower than 5 x 10(-6) s(-1). At the strain rate of 1 x 10(-6) s(-1), the SCC susceptibility index (I-SCC) is 0.96 and the elongation-to-failure (epsilon(f)) is only 0.11%. Fractography indicates that the brittle quasi-cleavage feature is very obvious and become more pronounced with decreasing the strain rate. Further analysis confirms that the cracking mode is predominantly transgranular, but the partial intergranular cracking at some localized area can also occur. Meanwhile, it seems that the crack propagation path is unrelated to the existing phase particles. Copyright 2014, National Engineering Research Center for Magnesium Alloys of China, Chongqing University. Production and hosting by Elsevier B.V. Open access under CC BY-NC-ND license.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据