Cold spray; Fatigue; Aluminum alloys
资金
- ONR [N00014-15-1-2133]
- ASGC NASA Training Grant [NNG05GE80H]
This paper examines the fatigue properties of freestanding AA7075 and AA2024 Cold Spray (CS) deposits. In this study, high pressure cold spray was used to make deposits large enough to machine mechanical test specimens free from the substrate. To quantify the mechanical performance, monotonic tensile and stress-controlled fatigue experiments were carried out on the freestanding CS and wrought AA7075 and AA2024 specimens. The experimental fatigue results revealed a reduction in the stress-life behavior of the CS deposits compared to the corresponding wrought material. However, when normalized by their ultimate tensile strengths, the CS specimens compared very well with the wrought materials, especially for the CS AA7075. Post-mortem analysis of the CS specimens revealed that fatigue cracks typically initiated from layer interface defects and subsequent crack propagation was influenced by the CS prior-particle boundaries. The results from this study indicate that refining the layer interface bonding may increase the fatigue resistance of freestanding aluminum alloy CS deposits.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据