INTERNATIONAL JOURNAL OF BIOLOGICAL MACROMOLECULES
卷 113, 期 -, 页码 171-178出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.ijbiomac.2018.02.117
关键词
Polyvinyl alcohol; Cellulose nanocrystal; Cross-linked network
资金
- National Natural Science Foundation of China [51403187]
- 521 Talent Project of Zhejiang Sci-Tech University [17010078-N]
- Candidates of Young and Middle Aged Academic Leader of Zhejiang Province [111103331271703]
Cross-linked polyvinyl alcohol (PVA) composite films with high structural stability were prepared by free radical copolymerization between cellulose nanocrystal (CNC) and maleic anhydride (MAH) modified PVA through spraying Fenton free radical as initiator. The influence of chemical cross-linked and physical network structure on mechanical, thermal and water absorption properties of the composite films were investigated. Compared to PVA and PVA/CNC composite film, significant improvements in the mechanical, thermal and water uptake properties of the cross-linked composite film were found. The tensile strength of the cross-linked composite film was enhanced from 23.1 MPa (neat PVA film) and 32.6 MPa (PVA/CNC-10%) to 42.5 MPa, and the maximum thermal degradation temperature was increased from 266.8 degrees C and 281.2 degrees C to 366.7 degrees C (cross-linked composite film). Besides, the water absorption was reduced from 385.9% and 220.6% to 175.7% for cross-linked composite film. It indicates that compared with physical network structure in PVA/CNC composite film, the multiple cross-linked networks showed excellent thermal stability, resistance of water swelling and structural stability at the same CNC loading level. Thus, the PVA/CNC composite film with the multiple cross-linked network shows greater property reinforcements. (C) 2018 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据