INTERMETALLICS
卷 92, 期 -, 页码 119-125出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.intermet.2017.10.002
关键词
Intermetallics (Ni-3(Si, Ti) alloys); Thermal properties; Microstructure; Physical properties
资金
- Japan Society for the Promotion of Science (JSPS) [26420663]
Thermal conductivities of Ni-3(Si,Ti) single-phase alloys with an L1(2) structure as functions of composition and temperature were measured to provide information for high-temperature structural applications. It was confirmed that the Ni-3(Si,Ti) alloy has an extremely large single-phase region for the compositions Ni-28(Si22-x,Ti-x) (x = 0-12 at.%), Ni89-y(Si-11,Ti-y) (y = 9.5-12 at.%), and Ni89-z(Si-z,Ti-11) (z = 9.5-12 at.%). The thermal conductivities at 293 K of all the Ni-3(Si,Ti) single-phase alloys were estimated to be between 8 W/mK and 12 W/mK, which are lower than those of almost all other stoichiometric compounds. In the Ni3(Si,Ti) single-phase region, the thermal conductivity increased more significantly by increasing the Ni content than by varying the Si and Ti contents. The thermal conductivity of all the Ni-3(Si,Ti) single-phase alloys increased monotonically with an increase in temperature. The temperature coefficient of thermal conductivity increased as the value of the thermal conductivity at 293 K was low, according to Mooij's relationship. Consequently, the thermal conductivity in the Ni-3(Si,Ti) single-phase region became larger and less sensitive to the composition at higher temperatures above 1073 K, ranging between 22 W/mK and 24 W/mK.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据