INTERMETALLICS
卷 92, 期 -, 页码 1-6出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.intermet.2017.09.005
关键词
Nb-Si alloy; Silicide; Directional solidification; Fracture toughness; Crack propagation
资金
- Academic Excellence Foundation of BUAA [2017009]
- National Natural Science Foundation of China [51471013, 51571004, 51404017]
The alloying effects of Ta and W on the phase composition, microstructure and room-temperature fracture toughness of Nb-Si based alloys were investigated. The nominal compositions of Nb-Si based alloys were Nb-15Si-24Ti-4Cr-2A1-2Hf (base alloy, at.%), Nb-15Si-24Ti-4Cr-2Al-2Hf-lTa (1Ta alloy, at%) and Nb-15Si-24Ti4-Cr-2A1-2Hf-1W (1W alloy, at.%). Results showed that the base alloy, 1Ta alloy and 1W alloy were composed of Nb solid solution (Nbss), alpha Nb5Si3 and small volumes of hexagonal gamma Nb5Si3 phases. The elements of Ta and W were primarily partitioned in the Nbss phases. The addition of Ta improved the fracture toughness of the base alloy from 10.2 to 12.2 MPa m(1/2), but the addition of W reduced the fracture toughness to 8.2 MPa m(1/2). The fracture of Nbss phases in the three alloys exhibited a cleavage fracture mode, and river patterns were created on individual facets, while the Nb5Si3 phases showed a brittle fracture mode with flat and featureless fracture surfaces. Different with base alloy and 1W alloy, 1Ta alloy involved the occurrence of secondary cracking as well as interface decohesion. The toughening mechanisms of Nb-Si based alloys with Ta and W additions were emphasized.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据