期刊
HIGH PERFORMANCE POLYMERS
卷 31, 期 3, 页码 310-320出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0954008318766217
关键词
Poly(arylene ether nitrile); crystallization; mechanical property; dielectric constant
资金
- National Natural Science Foundation of China [51773028, 51603029]
- National Postdoctoral Program for Innovative Talents [BX201700044]
Poly(arylene ether nitrile) (PEN) copolymers (HQ/RS-PEN) containing different proportions of hydroquinone (HQ-PEN) block and resorcinol (RS-PEN) block were synthesized, and their crystalline, mechanical, and dielectric properties were investigated. Three HQ/RS-PEN copolymers with 10%, 20%, and 30% of RS-PEN blocks were prepared via condensation polymerization of HQ and RS with 2,6-dichlorobenzonitrile. The PEN copolymers were characterized and confirmed by Fourier transform infrared spectroscopy, intrinsic viscosity, and thermal analyses. With the addition of RS-PEN block, the flexibility of PEN copolymers was increased. In addition, even though the high loading content of RS-PEN block was incorporated, the PEN copolymers still exhibited relatively high dielectric constant, whereas the dielectric loss decreased. Furthermore, to investigate the effect of treatment time and temperature on the physical properties of crystalline PEN copolymers, HQ/RS-PEN20 was isothermally treated at different temperatures (280 degrees C, 300 degrees C, 310 degrees C, 320 degrees C, and 330 degrees C) for a constant time and at a constant time for different hours (1, 2, 3, 4, and 5 h). After the optimization of the crystallization of HQ/RS-PEN polymer, excellent mechanical and dielectric properties of copolymers were obtained. The results showed that when isothermally treated at 320 degrees C for 2 h, the HQ/RS-PEN20 showed optimal properties of tensile strength of 117.6 MPa and dielectric constant of 4.07 at 1 kHz.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据