JOURNAL OF APPLIED PHYSICS
卷 117, 期 13, 页码 -出版社
AMER INST PHYSICS
DOI: 10.1063/1.4916719
关键词
-
资金
- Deutsche Forschungsgemeinschaft [Sonderforschungsbereich 595/D6]
- AdRIA Hesse state center for Adaptronics
The morphotropic phase boundary composition Bi-1/2 Na(1/2)TiO(3-20)mol. % Bi1/2K1/2TiO3 was chosen as initial material to do selective A-site aliovalent doping replacing Na and K by 1 at. % La, respectively. The materials were studied macroscopically by measuring dielectric and electromechanical properties. The Na-replaced material has a lower freezing temperature Tfr, lower remanent polarization and remanent strain, and thus a higher degree of ergodicity than the K-replaced material. These results are contrasted with local poling experiments and hysteresis loops obtained from piezoresponse force microscopy. The faster relaxation of the tip-induced local polarization and the lower remanent state in bias-on and -off loops confirm the higher degree of ergodicity of the Na-replaced material. The difference in functional properties is attributed to small variations in chemical pressure achieved through selective doping. Raman results support this working hypothesis. (C) 2015 AIP Publishing LLC.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据