The influence of cobalt loading (10-30 wt% Co) and pore size of SBA-15 support on the physico-chemical and catalytic performance of mesoporous Co/SBA-15 catalysts for the Fischer-Tropsch synthesis (FTS) reaction (T = 245 degrees C, P = 290 psig, H-2/CO = 2, and GHSV = 2000 h(-1)) has been investigated. Catalysts were characterized by N-2 adsorption-desorption, X-ray diffraction (XRD), electron microscopy, and temperature-programmed reduction (TPR). The dispersion of Co/SBA-15 decreased and the extent of cobalt reduction increased with increasing either the cobalt loading or pore size of SBA-15. A maximum CO conversion was found for the sample with 20 wt% Co loading. More methane and less C5+ hydrocarbons were produced over less reducible 10 wt% Co loaded sample. The 20Co/SBA-15 catalysts with larger pores led to larger cobalt crystallite size, lower dispersion and higher reducibility. CO conversion increased with the increase of pore size in the range studied. The 20Co/SBA-15 catalysts with larger cobalt crystallite size showed higher C5+ selectivity for the FTS. Finally, at comparable Co loading, CO conversion of Co/SBA-15 catalysts were to be about 2 times greater than a Co/SiO2 sample, with only a minor difference in product selectivity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据