期刊
ELECTROCHIMICA ACTA
卷 263, 期 -, 页码 596-609出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2018.01.081
关键词
Hydrothermal method; Oxygen reduction reaction; Fuel cell; Durability; Titania nanorods
资金
- CSIR-YSA [DU-MLP-0090]
- CSIR
We report a simple, scalable approach to improve interfacial characteristics of carbon semi-coated titania nanorods-supported-Pt with superior peak power density as compared to Pt/C with thin metal loading of 150 mu g cm(-2). Thin layer of carbon coated titania nanorod is synthesized by hydrothermal method. Carbon coated titania nanorods boosts the Pt oxygen reduction reaction activity than carbon. The crystal structure, dispersion of platinum nanoparticles, surface morphology and oxidation state are studied by X-ray diffraction, transmission electron microscopy and X-ray photoelectron spectroscopy, respectively. Studies using conventional three electrode setup shows that Pt/CCT-30 retains 48% of initial electrochemical surface area even after 40,000 potential cycles between 0.6 and 1.2 V. The solid fuel cell mode accelerated stress durability studies show that thin layer of carbon coated titania nanorods-Pt (Pt/CCT 30) significantly enhances stability and preserves 75% of initial fuel cell performance even after 10,000 potential cycles between 1 and 1.5 V. In comparison, only 20% of performance is retained for Pt supported on carbon after 3000 cycles. (c) 2018 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据