PMMA-ZrO2; P(VDF-HFP); Composite polymer electrolyte; In situ polymerization; Lithium ion battery
资金
- National Natural Science Foundation of China [51404038, 51472034, 51503020]
- Educational Commission of Hubei Province Foundation of China [B2016040]
- Yangtze Youth Talents Fund [2016cqr05]
Poly(vinylidene fluoride-hexafluoroprolene) (P(VDF-HFP))-based composite polymer electrolyte (CPE) membranes doped with organic-inorganic hybrid particles poly(methylmethacrylate)-ZrO2 (PMMA-ZrO2) are fabricated by phase inversion, in which PMMA is firstly successfully grafted onto the surface of the homemade nano-ZrO2 particles via in situ polymerization confirmed by FT-IR. XRD and DSC patterns show that adding PMMA-ZrO2 into the polymer matrix can decrease the crystallinity of the CPE membranes and TG curves indicate the CPE membranes possess desirable thermal stability. It can be found that the CPE membrane presents a uniform surface with abundant interconnected micro-pores when the added amount of PMMA-ZrO2 increases to 5 wt % vs. polymer matrix, in which the ionic conductivity at room temperature and tensile strength can be up to 3.595 mS cm(-1) and 26.18 MPa, respectively. In particular, the CPE membrane shows the minimum deformation of about 8% after being exposed at 160 degrees C for 1 h, and the electrochemical working window of the assembled Li/CPE/SS cell can be stable at 5.1 V (vs Li/Li+) at room temperature. Moreover, the LiCoO2/CPE/Li coin cell can deliver a specific capacity of 114.5 mAh g(-1) with 79.13% capacity retention at 2.0 C after 110 cycles. The results suggest that the as-fabricated P(VDF-HFP)-based CPE doped with 5 wt % organic-inorganic hybrid particles PMMA-ZrO2 can be a promising polymer electrolyte for lithium ion batteries. (C) 2018 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据