卷 34, 期 7, 页码 1003-1013出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.dental.2018.03.007
关键词
Dental composite material; Bis-GMA-free; Resin matrix; Conversion; Water sorption; Solubility; Flexural properties; Polymerization shrinkage cytotoxicity; Bisphenol A
Objective. Synthesize a new BPA- free monomer for use in methacrylate-based materials and evaluate critical properties of resin and composite materials based on the monomer. Methods. Bis-EFMA was synthesized through reaction between 9,9-bis[4-(2-hydroxyethoxy)-phenyl]fluorene and 2-(methacryloyloxy)ethyl isocyanate. Experimental Bis-EFMA-based resin (Bis-EFMA/TEGDMA =50/50, wt./wt.) and composite were prepared. Critical properties were investigated according to standard or referenced methods Bis-GMA/TEGDMA (50/50, wt./wt.) resin system, Bis-GMA-based composite and 3M ESPE Filtek (TM) Z250 were used as controls. Results. FT-IR and H-1 NMR spectra confirmed the structure of Bis-EFMA monomer. Cured resin materials: Bis-EFMA-based and Bis-GMA-based resins had nearly the same degree of conversion (p > 0.05); Bis-EFMA-based resin had significantly lower shrinkage, water sorption and solubility, and cytotoxicity than Bis-GMA-based resin (p <0.05); flexural properties of Bis-EFMA-based resin were all higher than those of Bis-GMA-based resin (p < 0.05). Cured composite materials: There was no significant difference in conversion (p > 0.05); Bis-EFMA-based composite had significantly lower shrinkage and solubility (p <0.05); water sorption of Bis-EFMA-based composite and Z250 were similar (p > 0.05), but lower compared to Bis-GMA-based composite (p <0.05); Bis-EFMA-based composite had the deepest curing depth (p < 0.05); Before water immersion, there was no significant difference in flexural strength between Bis-EFMA-based composite and each control composite (p > 0.05), while FS became lower than that of Z250 (p < 0.05), but higher than that of Bis-GMA-based composite (p <0.05) after water immersion; Flexural modulus of Bis-EFMA-based composite and Z250 were nearly the same (p > 0.05), higher than that of Bis-GMA-based composite (p < 0.05); Bis-EFMA-based composite showed less cytotoxicity than Bis-GMA-based composite and Z250 (p < 0.05). Significance. Bis-EFMA has potential as a substitute for Bis-GMA to prepare Bis-GMA- free dental composites. (C) 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据