Intercalation of cations into partially reduced molybdenum oxide for high-rate pseudocapacitors

Intercalation capacitance is emerging as a promising approach to increasing energy density of electrochemical capacitors. However, the number of materials capable of intercalating ions other than small H+ and Li+ is limited. Here we report a K+ preintercalated hydrogenated MoO3 (KyMoO3-x) with enhanced conductivity and widened interlayer gaps. Different cations (Mg2+, Na+, K+ and Li+) were able to intercalate along the (010) facet of KyMoO3-x with high intercalation capacitance (374 F/cm(3) at 0.5 A/g in 5 M LiCl). The cation intercalation behavior and the origin of the high capacitance have been systematically studied. Using artificial seawater as electrolyte, high volumetric capacitance (188 F/cm(3) at 0.5 Al g) and good rate handling were also achieved. The KyMoO3-x electrode also showed a similar capacitance (196 F/cm(3) at 0.5 A/g) and cycling performance (89% of initial capacitance maintained after 10,000 cycles) in natural seawater. When KyMoO3-x was fabricated into a symmetric pseudocapacitor with natural seawater as the electrolyte, the energy density and power density of the electrode reached 0.91 mWh/ cm(3) and 6.5 W/cm(3), respectively. The impressive results indicate KyMoO3-x is a promising high-power handling pseudocapacitor electrode material. (C) 2015 Elsevier BY. All rights reserved.