CONSTRUCTION AND BUILDING MATERIALS
卷 170, 期 -, 页码 235-244出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2018.03.031
关键词
Alkali activated mortar; POFA; GBFS; Alkaline solution; Envirmental-friendly mortar
资金
- UTM, Johor Bahru, Malaysia [16H94]
- Malaysian Ministry of Education [4B322, 15JO8, 4Y117]
- MOSTI Grant [4S090]
Environmental concern raised by the production of ordinary Portland cement (OPC), is behind the search for greener construction materials and remediation. One such material is alkali activated mortars (AAMs). It is well known that the high molarity of sodium hydroxide (12-16 M) and high content of sodium silicate (sodium silicate to sodium hydroxide higher than 2.5) have negative impacts on the environment. Driven by this idea, we prepared some binary alkali activated mortars by combining palm oil fuel ash (POFA) and ground blast furnace slag (GBFS) at varying ratios. The effect of low concentration alkaline solution on the fresh, mechanical and durable properties of alkali activated was determined. The ratio of sodium hydroxide (molarity 4 M) (NH) to sodium silicate (NS) in the mixture was kept at 0.75. Microstructures of the prepared alkali activated mortars were analyzed using SEM, XRD and FTIR measurements. The achieved high strength (approximate to 72 MPa at age of 28 days) of the alkali activated mortars was attributed to the synergy between GBFS and POFA. Partial replacement of GBFS with POFA was demonstrated to be beneficial for improving the compressive strength, durability and resistance against sulphuric acid attack. Meanwhile, calcium aluminium silicate hydrate (CASH) gel was discerned to be the main reaction product of POFA and GBFS in these binary systems. It was established that the proposed AAMs can contribute towards the development of sustainable materials. (C) 2018 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据