RSC ADVANCES
卷 5, 期 104, 页码 85506-85510出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c5ra16107j
关键词
-
资金
- Australian Research Council [LP110100451]
- Australian Research Council [LP110100451] Funding Source: Australian Research Council
A straightforward and direct preparation route for nanocrystalline BaFBr:Eu2+ by ball-milling is reported. We demonstrate that the as-prepared nanocrystalline powder becomes an efficient photostimulable X-ray storage phosphor upon annealing at temperatures in the range of 400 to 900 degrees C. The dependence of crystallite size, photoluminescence and storage phosphor properties on annealing temperature and annealing time was investigated and the optimal conditions were determined. After annealing at 900 degrees C for 1 h, the average crystallite size was found to be similar to 200 nm. In comparison with the typical similar to 5 mu m particles for conventional phosphors, the shape and size distribution of the crystallites may allow higher packing densities, resulting in higher sensitivities, and resolution in computed radiography. The photostimulable storage properties compare favorably with results obtained for a commercial BaFBr(I):Eu2+ imaging plate.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据