期刊
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
卷 112, 期 -, 页码 423-431出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2018.06.029
关键词
Poly(L-lactic acid); Nanoscale dispersed silica; Uniaxial stretching; Microporous structure
资金
- National Natural Science Foundation of China [51503204]
- Science and Technology Bureau of Jilin Province of China [20170204012SF]
- Chinese Science Academy (Changchun Branch) [2017SYHZ0018]
- National Key Research and Development Program of China [2016YFC0501402]
The microporous poly(L-lactic acid) (PLLA) was prepared successfully by uniaxial stretching PLLA with nanoscale dispersed silica as pore forming agent. The SEM results revealed that the silica dispersed uniformly in the PLLA matrix with the form of monodispersed nanoparticles or nanoscale aggregates when the content was 3-20 wt%. The number and size of the micropores and the porosity for the microporous PLLA were increased with the increase of silica content, stretching ratio and stretching rate (5-20 mm/min), while were reduced with the rise of stretching temperature. The stretching ratio of 2.5 was the key point for pore forming when silica content was under 10 wt%. The porosity was up to 21.1% with the silica content of 20 wt% and stretching ratio of 4.5. The mechanical properties and thermal insulation properties of microporous PLLA were also improved comparing with that of PLLA without pores.