期刊
CHINESE JOURNAL OF POLYMER SCIENCE
卷 36, 期 5, 页码 612-619出版社
SPRINGER
DOI: 10.1007/s10118-018-2041-y
关键词
Cu(OH)(2) nanowires; PVDF UF membrane; Oil-Water emulsion separation
资金
- Postdoctoral Science Foundation of China [2014M560802]
- Natural Science Foundation of Education Department of Shaanxi Provincial Government [16JK1755]
- State Key Laboratory of Chemical Engineering [SKL-ChE-16A04]
Cu(OH)(2) nanowires were prepared and incorporated into poly(vinylidene fluoride) (PVDF) to fabricate Cu(OH)(2)-PVDF ultrafiltration (UF) membrane via immersion precipitation phase inversion process. The effect of Cu(OH)(2) nanowires on the morphology of membranes was investigated by X-ray photoelectron spectroscopy (XPS), Fourier transform infrared (FTIR) spectroscopy, atomic force microscopy (AFM), scanning electron microscopy (SEM) and X-ray diffraction (XRD) measurements. The results showed that all the Cu(OH)(2)-PVDF membranes had wider fingerlike pore structure and better hydrophilicity, smoother surface than pristine PVDF membrane due to the incorporation of Cu(OH)(2) nanowires. In addition, water flux and bovine serum albumin (BSA) rejection were also measured to investigate the filtration performance of membranes. The results indicated that all the Cu(OH)(2)-PVDF membranes had high water flux, outstanding BSA rejection and excellent antifouling properties. It is worth mentioning that the optimized performance could be obtained when the Cu(OH)(2) nanowires content reached 1.2 wt%. Furthermore, the membrane with 1.2 wt% Cu(OH)(2) nanowires showed outstanding oil-water emulsion separation capability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据